Graphite |
Carbon-graphites menawarkan engenering design yang unik . Manufactured entirely from carbon and including high temperature carbonaceous bonding, these materials combine the strength, hardness and wear resistance of carbon with the corrosion resistance and self lubricating properties of graphite. The precisely controlled inherent porosity of carbon-graphites can be filled with a variety of impregnants to enhance chemical, mechanical and tribological properties.
|
| Types of Carbon |
| Kata carbon biasanya digunakan sebagai sinonim dari kata Grafit. This is unfortunate since each form of the element carbon offers specific properties that can be used to benefit different types of applications.
Amorphous Carbon |
| Amorphous carbon is a very hard, strong compound. The crystals exhibit a turbostratic disorder which makes the material extremely resistant to wear. The strength and wear resistance properties of this material make it of interest in some applications. However, these strengths can also be a weakness -carbon generates high friction when rubbed against another surface.
Graphite |
| Graphite, on the other hand, is softer and relatively weak because of the crystalline order and closer spacing between the monoplanes and stacks. A graphite structure can be compared to a deck of cards with individual layers able to easily slide off the deck. This phenomenon gives the material a self lubricating ability which is matched by no other material. External lubricants are simply not necessary.
|
| Carbon-Graphites |
| It is possible to combine amorphous carbon and graphite to take full advantage of the strengths and weaknesses of each of these two types of carbon. The proper mixture of the two materials is strong and hard and has low friction. At the same time, this composite has excellent corrosion resistance and is capable of operating at temperatures in excess of 450°C for extended periods of time, depending on the specific grade. The ability to create materials that have these properties is the basis of the manufactured mechanical carbon materials that perform well in difficult tribological situations such as pumps.
|
| Processing Carbon-Graphites |
| Carbon-graphites are created by combining the two forms of carbon with coal tar pitch. The coal tar pitch acts as a temporary binder that holds the two structures together during the compression moulding process in which near net shapes are formed. Following the moulding operation, the parts are sintered at temperatures high enough to carbonise the coal tar pitch. The result is a structure that is completely carbon bound and contains both carbon and graphite. This structure is extremely strong in compression and will not creep under load. The carbonisation of the temporary binder leaves holes in the structure - on a micro scale the sintered body is a black sponge.
The formation of holes during the processing of a carbon-graphite composite has various advantages. The holes can be filled with resins, metals, carbon, or inorganic salts, depending on the planned use of the material. |
| These fillers serve to improve the strength, thermal conductivity ,corrosion and wear characteristics of the material. Additionally, carbon-graphite can be sintered to an even higher temperature to convert the entire structure to graphite to provide especially good performance in very high temperature, high speed applications. |
| Impregnation Application |
| Thermoset resin General duty to 260°C in water, coolants, fuels, oils. Light chemical solutions, food and drug.
Antimony, Hot water, steam, light hydrocarbons.Copper or silver.
Carbon Highly corrosive environments.
Film formers (fluorides etc) by using,CVD ,CVR , vacuum process etc.
Oxidation inhibitors (inorganic salts solution) for High temperature and/or high speed (to 850°C ,500 RPM).
|
| Carbon-Graphites vs Traditional Lubricants |
| Carbon-graphites are used in a wide range of applications where traditional lubricating methods are not appropriate. For example, a typical oil lubricated bearing struggles at temperatures below -40°C because of the high viscosity of the oil. Above 200°C oils carbonise, making them abrasive and ineffective. Graphite bearings are capable of extended use at temperatures above 600°C.
|
| Chemically Aggressive Environments |
| Chemically aggressive applications represent another application niche for carbon-graphite. For instance, sterilisation processes tend to leach the oil from the structure of an oil lubricated bearing. Also, solvents and radiation can break down lubricating oils, and low pressures can cause the oil to vaporise. Carbon-graphite materials are inherently stable and chemically resistant, making them ideally suitable for these types of application.
|
| Inside of a pump. The four vanes on the rotor are made of carbon-graphite, and are consequently self lubricating, temperature resistant and impermeable to gases and liquids.
|
| High Load Applications |
| Lubricants are inappropriate in other applications for a variety of reasons. High loads can squeeze the lubricant from a surface. Without the hydrodynamic layer of lubricant, failure is imminent if the material cannot provide self lubrication. In some applications, such as those involving food handling, lubricants can contaminate the surrounding environment. Specific grades of carbon-graphites are approved for use in food handling applications.
|
| Design Factors |
|
Carbon-graphite bearings are used in both wet and dry operating conditions. Carbon-graphite allows the designer to specify the bearing close to the boundary lubricated condition without the risk of seizure. Permissible loads and running speeds depend on the allowable wear rate. Shaft materials and surface finishes are important factors in the wear rates of carbon-graphite materials. As a rule of thumb, the harder and more polished the surface, the lower the wear. Where possible, aluminium and bronze should be avoided for use as shaft materials.
|
| Applications |
| Carbon-graphite materials are also widely used as rotating shaft and face seal materials. They perform well when running against metal and ceramic counterfaces. Seals are manufactured from solid rings, split rings and segmented rings for use in both liquid and dry-running applications in the aerospace, nuclear, petrochemical and general marine industries.
|
| Carbon-graphite seals are self lubricating, resistant to chemical corrosion, and capable of running at temperatures up to 538°C.
Carbon-Graphite Seals
Seal materials require high strength and a relatively high modulus of elasticity to withstand deformation at the interface. Carbon-graphite seal materials provide the strength and rigidity which are especially important in high pressure, zero leakage mechanical end-face seals. High thermal conductivity is essential in removing heat from the interface.
Seal wear is a result of adhesive wear, chemical wear, erosive wear and sometimes radioactive wear. Carbon-graphite is inert to most chemical reagents so it survives where other materials fail. However, chemical wear is evidenced in certain strong oxidising environments or where the additives are attacked by specific oxidising reagents.
|
| Impregnation of Carbon-Graphite Seals |
| Impregnation of carbon materials can be done with a variety of materials to control permeability. In addition to thermoset resins, other types of impregnants include thermoplastics, metals, and inorganic salts or glasses. The temperature limit of the impregnant places an upper limit on the operating temperature of the carbon parts.
Metals such as antimony, silver and ceramics can improve the strength, thermal conductivity, and trilogical characteristics of the materials. Impregnants made of inorganic salts solution - and glasses are used in high temperature applications. Carbons impregnated with soluble salts must be handled carefully to avoid exudation, especially under humid conditions, but loss of impregnant rarely affects any physical property of a seal other than permeability.
Special process are available that provide corrotion and wear resistance up to 900°C or more.
|
| Blistering |
| Blistering is a critical concern with carbon seal materials. Strangely, the reason why blistering occasionally occurs is not clear. One of the most popular explanations is that a certain amount of fluid becomes absorbed in the carbon substrate and expands due to frictional heat, creating a subsurface pressure and eventual crater in the seal face. Another theory is that softer mating materials can tend to tear pieces from the carbon-graphite in the presence of heavy hydrocarbons. Blistering is most often found in applications involving hydrocarbons or cyclical temperature service such as air conditioning compressors. In some cases, the use of silicon carbide as a mating surface will reduce or even eliminate a blistering problem, possibly because of its high thermal conductivity and hardness.
Carbon-Graphite Seals in Aerospace Applications
Carbon-graphite and graphites are excellent materials for aircraft turbine engine mainshaft seals. The mainshaft in a turbine engine rotates at very high speeds and operates in an environment of changing high temperature conditions. Mainshaft bearing compartment seals are used to protect rotor support bearings from hot gases flowing through the engine and to prevent the loss of lubricant in the bearing compartments.
|
| Materials Selection and Suitability |
| Loads, speeds, temperatures, mating materials, cost constraints and projected volume are critical factors to be kept in mind when selecting materials. Scores of base carbon materials are available with hundreds of modifications that can be customised for specific designs and environments. General service carbon-graphites are usable up to 450°C while special grades are available that provide resistance up to 538°C. Special carbons and impregnants are used for seal applications ,shaft ,rotors in the 260-900°C temperature range or more.
These materials are chemically inert, temperature resistant, lightweight, resilient, dimensionally stable, and impermeable to gases and liquids. They can be moulded to size or machined to close tolerances, impregnated, plated, vulcanised to rubber, and cemented.
|
| |
| |
|
| |
| |
| |
|